We export ceramic raw materials produced in midland Japan, which is the center of the Japanese ceramic industry.
Efficient Feldspar Powder production line equiped full automatic packing & palleting system enable us to manage urgent orders. Under thorough quality control system, we can continually supply quality stable ceramic raw materials worldwide.
Feldspar Powder for Oxidation Firing
Wide-range melting temperature creates stable clear colors especially in colored glazes.
| SiO2 | Al2O3 | Fe2O3 | CaO | K2O | Na2O | Igloss |
|---|---|---|---|---|---|---|
| 77.56% | 12.25% | 0.09% | 0.56% | 5.05% | 3.46% | 0.35% |
Refractoriness：SK8
Gairome Clay
Gairome Clay is the Japanese representative of high plastic clay.It has a rich plasticity and high refractoriness.
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | Igloss |
|---|---|---|---|---|---|---|---|---|
| 49.05% | 34.05% | 1.24% | 0.82% | 0.19% | 0.18% | 0.82% | 0.09% | 13.30% |
Refractoriness：SK35
Compounded Body Clays
Clays for pottery body consisting of Pottery Stone, Kaolin, Kibushi Clay and Gairome Clay etc. Firing temperature of "1-S" & "NA-6" is both 1250～1300℃(centigrade).
Under oxidation firing condition, "NA-6" can get more white color.
Also "NA-6" is specially tough body clay and easy to produce bigger size products. "1-S" & "NA-6" both have good transparency.
Product No.1-S
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | Igloss |
|---|---|---|---|---|---|---|---|---|
| 68.06% | 20.03% | 0.74% | 0.19% | 0.25% | 0.14% | 3.54% | 1.22% | 5.57% |
Refractoriness：SK12 / Contraction rate：13% / Used in casting and machine forming
Product No.NA-6
| SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | Igloss |
|---|---|---|---|---|---|---|---|---|
| 66.24% | 20.98% | 0.52% | 0.24% | 0.29% | 0.23% | 3.66% | 1.23% | 6.61% |
Refractoriness：SK12 / Contraction rate：13% / Used in hand-making, casting and machine forming
*We can create new compounds and produce new body clay to match your request. Please inform us of your needs.